Harris DynaFlow 15% 3.2mm
DETAILS
Dynaflow® melts and flows at temperatures very close to Stay-Silv® 15 and provides comparable brazed mechanical properties. This makes Dynaflow® an excellent cost-effective alternative to the 15% silver alloys. This premium, medium range silver alloy has been meticulously formulated to even tighter specifications than our standard copper-to-copper alloys.
Features
Premium, medium-range, alloy for brazing copper or brass.
Excellent strength and ductility.
Economical replacement of 15% silver alloys.
When heated above its liquidus, can penetrate tight connections.
Wide melting range provides ability to fill loose connections and "cap" or "build-up" around the finished joint.
Self-fluxing on copper and copper-to-copper connections. Use Stay-Silv® white flux for brazing brass or copper-to brass.
Corrosion resistance is generally similar to the copper base metal
Not recommended for brazing steel or other ferrous base metals
Due to its phosphorus content, should not be used if the braze is exposed to sulfur or sulfur compounds in service.
Complies with the EU Reach & RoHS directive
Typical Applications
Copper-to-copper brazing
DETAILS
Dynaflow® melts and flows at temperatures very close to Stay-Silv® 15 and provides comparable brazed mechanical properties. This makes Dynaflow® an excellent cost-effective alternative to the 15% silver alloys. This premium, medium range silver alloy has been meticulously formulated to even tighter specifications than our standard copper-to-copper alloys.
Features
Premium, medium-range, alloy for brazing copper or brass.
Excellent strength and ductility.
Economical replacement of 15% silver alloys.
When heated above its liquidus, can penetrate tight connections.
Wide melting range provides ability to fill loose connections and "cap" or "build-up" around the finished joint.
Self-fluxing on copper and copper-to-copper connections. Use Stay-Silv® white flux for brazing brass or copper-to brass.
Corrosion resistance is generally similar to the copper base metal
Not recommended for brazing steel or other ferrous base metals
Due to its phosphorus content, should not be used if the braze is exposed to sulfur or sulfur compounds in service.
Complies with the EU Reach & RoHS directive
Typical Applications
Copper-to-copper brazing
DETAILS
Dynaflow® melts and flows at temperatures very close to Stay-Silv® 15 and provides comparable brazed mechanical properties. This makes Dynaflow® an excellent cost-effective alternative to the 15% silver alloys. This premium, medium range silver alloy has been meticulously formulated to even tighter specifications than our standard copper-to-copper alloys.
Features
Premium, medium-range, alloy for brazing copper or brass.
Excellent strength and ductility.
Economical replacement of 15% silver alloys.
When heated above its liquidus, can penetrate tight connections.
Wide melting range provides ability to fill loose connections and "cap" or "build-up" around the finished joint.
Self-fluxing on copper and copper-to-copper connections. Use Stay-Silv® white flux for brazing brass or copper-to brass.
Corrosion resistance is generally similar to the copper base metal
Not recommended for brazing steel or other ferrous base metals
Due to its phosphorus content, should not be used if the braze is exposed to sulfur or sulfur compounds in service.
Complies with the EU Reach & RoHS directive
Typical Applications
Copper-to-copper brazing